60# Estate Label® #12 Vellum - White 100% PCW Wet Strength, FSC® Certified Optimized for HP Indigo Presses / H-318 / 1.2 Mil Clear 90% Recycled Polyester (rPET)

  • Warehouse: WI

60# Estate Label® #12 Vellum - White 100% PCW Wet Strength, FSC® Certified Optimized for HP Indigo Presses : see other catalog options

Elegant white facestock with a vellum finish that easily accepts die-cutting, embossing, and foil stamping. It is manufactured with "wet strength" properties to increase performance in moist environments. The Estate grades are FSC® Certified. It is suitable for high-speed bottling and packaging lines. It is a great stock for premium and prestigious labeling such as wine bottles and home-craft labeling applications. This product is also manufactured 100% PCW. Top coated and optimized for HP Indigo Presses.

Basis Weight (25 x 38 / 500) 60 lbs.
Caliper 4.8 mils
Brightness, MacBeth 89 %
Opacity, Huygen 93 %
Tensile, lbs.(dry)/15 mm, MD / CD 9 / 7 lbs/15mm
Smoothness, Hagerty 240 units
Regulatory Compliances FSC® Certified, FSC® is a voluntary program, and not legally required to be adhered to

H-318 : see other catalog options

H-318 is the ideal choice for high end beverage and spirits, with improved resistance to moisture and humidity after bottling and at presentation to the consumer. H-318 is an aggressive, blended emulsion acrylic adhesive with the unique ability to combine special characteristics from different adhesives. H-318 was engineered to provide excellent high initial tack and quicker label adhesion onto glass while providing functional converting performance on an array of paper and film face stocks.

Type Hybrid
Classification Emulsion Acrylic
Minimum Application Temp. 35 °F
Service Temperature Range +10 to +150 °F
Regulatory Compliances FDA 21 CFR 175.105

1.2 Mil Clear 90% Recycled Polyester (r-PET) : see other catalog options

A clear 90% recycled content polyester film liner with high strength and durability. Typically used for high speed automatic roll-to-roll applications.

Caliper 1.2 mils
Yield 16,800 sq. in/lb
Elongation at break, MD / TD 140 / 135 %
Haze 3.2 %
Tensile Strength, MD / TD 25,600 / 27,200 psi
Shrinkage at 302°F/30 min., MD / TD 1.6 / .2 %