Roll Label Materials
Roll Label Materials

W034962

60# Estate Label® #14 Smooth - Bright White 100% PCW Wet Strength, FSC® Certified, Optimized for HP Indigo Presses / H-318 / 1.2 Mil Clear 90% Recycled Polyester (r-PET)

QUANTITY:
Specifications
  • Warehouse: WI

60# Estate Label® #14 Smooth - Bright White 100% PCW Wet Strength, FSC® Certified, Optimized for HP Indigo Presses : see other catalog options

Bright white uncoated premium paper facestock with a smooth finish manufactured with 100% post-consumer fibers. The Estate Label #14 is FSC certified and meets the mark of responsible forestry. This facestock also has wet strength characteristics to increase performance in moist environments. It easily accepts die-cutting, embossing and foil stamping. It is a great stock to complement your brand image. Top coated and optimized for HP Indigo Presses.

Basis Weight (25 x 38 / 500) 60 lbs.
Caliper 4.4 mils
Regulatory Compliances FSC® Certified, FSC® is a voluntary program, and not legally required to be adhered to

H-318 : see other catalog options

H-318 is the ideal choice for high end beverage and spirits, with improved resistance to moisture and humidity after bottling and at presentation to the consumer. H-318 is an aggressive, blended emulsion acrylic adhesive with the unique ability to combine special characteristics from different adhesives. H-318 was engineered to provide excellent high initial tack and quicker label adhesion onto glass while providing functional converting performance on an array of paper and film face stocks.

Type Hybrid
Classification Emulsion Acrylic
Minimum Application Temp. 35 °F
Service Temperature Range +10 to +150 °F
Regulatory Compliances FDA 21 CFR 175.105

1.2 Mil Clear 90% Recycled Polyester (r-PET) : see other catalog options

A clear 90% recycled content polyester film liner with high strength and durability. Typically used for high speed automatic roll-to-roll applications.

Caliper 1.2 mils
Yield 16,800 sq. in/lb
Elongation at break, MD / TD 140 / 135 %
Haze 3.2 %
Tensile Strength, MD / TD 25,600 / 27,200 psi
Shrinkage at 302°F/30 min., MD / TD 1.6 / .2 %