W027885

60# Estate Label® #9 Wet Strength, FSC® Certified / H-318 / 1.2 Mil Clear Polyester

QUANTITY:
Specifications
  • Warehouse: WI, NV

60# Estate Label® #9 Laid Wet Strength, FSC® Certified : see other catalog options

Elegant cream facestock with a laid finish that easily accepts die-cutting, embossing, and foil stamping. It is manufactured with "wet strength" properties to increase performance in moist environments. The Estate grades are FSC® Certified as well as alkaline and made with archival properties for a longer life. It is suitable for high-speed bottling and packaging lines. It is a great stock for premium and prestigious labeling such as wine bottles and home-craft labeling applications.

Basis Weight (25 x 38 / 500) 60 lbs.
Caliper 5.4 mils
Brightness, MacBeth 73 %
Opacity, Huygen 91 %
Tensile, lbs.(dry)/15 mm, MD / CD 15+ / 8+ lbs/15mm
Smoothness, Hagerty 310 units
pH Alkaline
Regulatory Compliances FSC® Certified, FSC® is a voluntary program, and not legally required to be adhered to, Archival

H-318 : see other catalog options

H-318 is the ideal choice for high end beverage and spirits, with improved resistance to moisture and humidity after bottling and at presentation to the consumer. H-318 is an aggressive, blended emulsion acrylic adhesive with the unique ability to combine special characteristics from different adhesives. H-318 was engineered to provide excellent high initial tack and quicker label adhesion onto glass while providing functional converting performance on an array of paper and film face stocks.

Type Hybrid
Classification Emulsion Acrylic
Minimum Application Temp. 35 °F
Service Temperature Range +10 to +150 °F
Regulatory Compliances FDA 21 CFR 175.105

1.2 Mil Clear Polyester : see other catalog options

A clear polyester film liner with high strength and durability. Typically used for high speed automatic roll-to-roll applications.

Caliper 1.2 mils
Yield 16,500 sq. in/lb
Tensile Strength, MD / TD 29,900 / 29,900 psi
Haze 3.5% %
Elongation at break, MD / TD 100 / 100 %
Shrinkage at 302°F/30 min., MD / TD 2 / 0.4 %
Regulatory Compliances CONEG, REACH